Pengaruh Treatmen Pencucian Terak Alumunium Pada Pembuatan Batu Gerinda

Efrendy, Angga and , Bambang Waluyo F, ST. MT (2018) Pengaruh Treatmen Pencucian Terak Alumunium Pada Pembuatan Batu Gerinda. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (NASKAH PUBLIKASI) NASKAH PUBLIKASI.pdf Download (1MB)
	PDF (HALAMAN DEPAN) HALAMAN DEPAN.pdf Download (1MB)
	PDF (BAB I) BAB I.pdf Download (143kB)
	PDF (BAB II) BAB II.pdf Restricted to Repository staff only Download (589kB)
	PDF (BAB III) BAB III.pdf Restricted to Repository staff only Download (819kB)
	PDF (BAB IV) BAB IV.pdf Restricted to Repository staff only Download (377kB)
	PDF (BAB V) BAB V.pdf Restricted to Repository staff only Download (87kB)
	PDF (DAFTAR PUSTAKA) DAFTAR PUSTAKA.pdf Download (89kB)
	PDF (LAMPIRAN) LAMPIRAN.pdf Restricted to Repository staff only Download (570kB)
	PDF (PERNYATAAN PUBLIKASI) PERNYATAAN PUBLIKASI.pdf Restricted to Repository staff only Download (315kB)

Abstract

Grinding is a tool used for the process of reducing and cutting an abrasive workpiece through friction between the abrasive material and the workpiece. In addition, the grinding process can also for the process of finishing workpieces (refine the workpiece surface) smoothed the pieces, welding results, can also as a metal sharpener such as knives and chisels. In this research, the manufacture of self-assembled grinding wheels with aluminum slag materials that have been washed as abrasion material that aims to find out how much the rate of wear and grind own specimen grinding wheels, previous research, and the existing grinding wheels in the market market with Lippro brand. The process of making the grinding wheel begins with the preparation of materials to be used, namely liquid phenolic resin and powder, cast aluminum slag, mesh 12 and 40 that have been washed and fiberglass mesh fiber. After that mix all the ingredients according to the composition that has been determined. Furthermore 2 all materials are inserted in the mold and compressed with a press machine with a 15 ton force for 5 minutes. Then ignored at room temperature of at least 24 hours. Then sintered with temperature 1400C for 1 hour. Tests performed are wear test with ASTM D-3702 standard. From the results of research shows that the wear value of Lippro brand grinding wheel has a low wear rate compared to homemade grinding stone.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	grinding stone, phenolic resin, aluminum slag
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ANGGA EFRENDY
Date Deposited:	03 Feb 2018 06:47
Last Modified:	18 Nov 2019 04:18
URI:	http://eprints.ums.ac.id/id/eprint/59093

Actions (login required)

View Item