Pengaruh Komposisi Mangan Terhadap Ketahanan Aus Pada Besi Cor Kelabu

Setyawan, Dhanindra Albani and , Agung Setyo Darmawan, ST. MT (2025) Pengaruh Komposisi Mangan Terhadap Ketahanan Aus Pada Besi Cor Kelabu. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (407kB)
	PDF (Halaman Depan) Halaman Depan.pdf Download (938kB)
	PDF (Bab I) BAB I.pdf Download (429kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (706kB)
	PDF (Bab III) BAB IV.pdf Restricted to Repository staff only Download (1MB)
	PDF (Naskah Publikasi) D200200038_Naskah Publikasi.pdf Download (909kB)
	PDF (Daftar Pustaka) Daftar Pustaka.pdf Download (499kB)
	PDF (Lampiran) Lampiran.pdf Restricted to Repository staff only Download (1MB)
	PDF (Surat Pernyataan Publikasi) D200200038_Surat Pernyataan Publikasi.pdf Restricted to Repository staff only Download (1MB)

Abstract

This research aims to determine the effect of manganese composition on the wear resistance of gray cast iron. The research process that will be carried out includes several tests, namely testing Chemical Composition, Microstructure and Wear Resistance. Chemical composition testing was carried out using a spectrometer, then microstructure (metallography) using a SEM EDS tool, and wear resistance using an Ogoshi wear resistance test tool. The results of chemical composition testing show that the higher the addition of manganese elements, the higher the percentage of manganese in gray cast iron. The results of metallographic tests show that all materials are dominated by graphite and pearlite phases, then the higher the addition of manganese elements to the gray cast iron, the larger the graphite shape and the thicker the size. The results of wear resistance testing show that the higher the addition of manganese to gray cast iron, the more wear resistant it is.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Gray cast iron, Chemical composition, Microstructure, Wear Resistance
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > S1 Teknik Mesin
Depositing User:	DHANINDRA ALBANI SETYAWAN
Date Deposited:	06 May 2025 02:45
Last Modified:	06 May 2025 02:45
URI:	http://eprints.ums.ac.id/id/eprint/133935