Analisa Sifat Mekanis Dan Struktur Mikro Baja SS 400 Setelah Carburizing Menggunakan Arang Kayu Asem Dan Quenching Dengan Oli Dan Air

Setyo Cahyono, Jatmiko and -, Ir. Supriyono, M.T., Ph.D (2022) Analisa Sifat Mekanis Dan Struktur Mikro Baja SS 400 Setelah Carburizing Menggunakan Arang Kayu Asem Dan Quenching Dengan Oli Dan Air. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN.pdf Restricted to Repository staff only Download (271kB)
	PDF (Naskah Publikasi) NASKAH PUBLIKASI.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (716kB)
	PDF (Bab I) BAB I.pdf Download (138kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (693kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (707kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (84kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (957kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (539kB)

Abstract

This study aims to determine the effect of Asem wood charcoal in the heat treatment process using the carburizing method on SS 400 steel on mechanical properties and microstructure.In this study, the carburizing medium used was tamarind wood charcoal with a weight percentage of 60% and a CaCo3 catalyst of 40%. The temperature used is 8500C with a holding time of 60 minutes with a variation of 15w-40 oil and water quenching media.The results of the tensile test show that the carburizing material with variations of oil and water quenching media has more brittle properties than the raw material. The surface hardness value for raw material is 191.53 VHN, while for carburizing material with oil quenching media it is 412.00 VHN, while for carburizing material with water quenching media it is 508.64 VHN. The results of micro photos of carburizing material with water quenching media have a pearlite phase which is more dominant than raw material and carburizing material with oil quenching media.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Keywords: carburizing, quenching, tensile, hardness, microstructure.
Subjects:	T Technology > T Technology (General)
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	JATMIKO SETYO CAHYONO
Date Deposited:	24 Feb 2022 02:51
Last Modified:	24 Feb 2022 02:51
URI:	http://eprints.ums.ac.id/id/eprint/98598

Actions (login required)

View Item