Carburizing Baja Karbon Rendah Arang Kayu Sengon Dengan Proses Pendinginan Menggunakan Air Dan Oli Dengan Viskositas 10w - 40

Ishmata Agnatia, Devan and , H. Supriyono, S.T.,M.T.,Ph.D (2021) Carburizing Baja Karbon Rendah Arang Kayu Sengon Dengan Proses Pendinginan Menggunakan Air Dan Oli Dengan Viskositas 10w - 40. Skripsi thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
Naskah Publikasi.pdf

Download (1MB)
[img] PDF (Halaman Depan)
Halaman Depan.pdf

Download (1MB)
[img] PDF (Bab I)
BAB I.pdf

Download (52kB)
[img] PDF (Bab II)
BAB II.pdf
Restricted to Repository staff only

Download (286kB) | Request a copy
[img] PDF (Bab III)
BAB III.pdf
Restricted to Repository staff only

Download (955kB) | Request a copy
[img] PDF (Bab IV)
BAB IV.pdf
Restricted to Repository staff only

Download (16kB) | Request a copy
[img] PDF (Daftar Pustaka)
Daftar Pustaka.pdf

Download (27kB)
[img] PDF (Lampiran)
Lampiran.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] PDF (Surat Pernyataan Publikasi)
Surat Pernyataan Publikasi.pdf
Restricted to Repository staff only

Download (488kB) | Request a copy

Abstract

The purpose of this research is carburizing low carbon steel, sengon wood charcoal by cooling process using water and oil with a viscosity of 10W- 40. In this study, a study of Bengkirai wood charcoal particles produced from incomplete combustion and using the collision method with the shaker mills model was carried out. Carburizing by cooling using water and oil with micro test, hardness and tensile to find out how much influence on material changes, to determine the hardness of the material, to determinethe mechanical properties. The results of the microstructure test, pack carburizing with cooling using SAE 10W-40 oil has a large number of pearlite crystals from ferrite crystals. The result of pack carburizing hardness test by cooling using water has the highest value with an average value of 471.8 VHN. Tensile test results of pack carburizing by cooling using water have the highest tensile strength with an average value of 632.27 MPa

Item Type: Karya ilmiah (Skripsi)
Uncontrolled Keywords: carburizing, pendinginan, Arang Sengon, struktur mikro, kekerasan, tarik
Subjects: Q Science > Q Science (General)
T Technology > T Technology (General)
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: DEVAN ISHMATA AGNATIA
Date Deposited: 17 Nov 2021 06:32
Last Modified: 17 Nov 2021 06:33
URI: http://eprints.ums.ac.id/id/eprint/95839

Actions (login required)

View Item View Item