Analisis X-Ray Diffraction (XRD) Pada Brazing Antara Aluminium Seri 6061 Dengan Penambahan Filler Alusol Dan Filler Lokal

Nugroho, Anggara Dwiky and -, Agus Dwi Anggono, ST, M.Eng, Ph.D (2020) Analisis X-Ray Diffraction (XRD) Pada Brazing Antara Aluminium Seri 6061 Dengan Penambahan Filler Alusol Dan Filler Lokal. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI.pdf Download (773kB)
	PDF (Halaman Depan) Anggara_HALAMAN AWAL.pdf Download (780kB)
	PDF (Bab I) BAB I.pdf Download (95kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (659kB) | Request a copy
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (197kB) | Request a copy
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (186kB) | Request a copy
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (60kB) | Request a copy
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (45kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (951kB) | Request a copy
	PDF (Surat Pernyataan Publikasi) Surat Pernyataan Publikasi.pdf Restricted to Repository staff only Download (172kB) | Request a copy

Abstract

The purpose of this study was to determine the crystal structure and compounds formed in the connection area of aluminium and aluminium plates with alusol fillers and local fillers using brazed joints. The material used in this study is aluminum 6061 series, alusol filler, and local filler. In this study the standard for specimen making is ASME IX, XRD testing is used to determine the crystal structure and compounds formed in the brazed junction region. The results showed that the first material formed was Brazing between Aluminum and Aluminum using alusol filler formed 〖 Al〗_4 C_3 compound had the highest peak at an angle of 65.38 ° with an intensity of 628 cps. The crystal structure is Rhombohedral and a density of 2,998 g/〖cm〗^3, the second Brazing between Aluminium and Aluminium using a local alloy filler formed SiC compound has the highest peak at an angle of 38.78 ° with an intensity of 7602 cps. The crystal structure is Hexagonal and a density of 3,174 g/〖cm〗^3, and the Compound 〖 Al〗_4 C_3 has the highest peak at an angle of 78.52 ° with an intensity of 522 cps, the crystal structure is Rhombohedral and density of 2,998 g/〖cm〗^3.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	Brazed, X-ray Diffraction, Crystal Structure, filler
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ANGGARA DWIKY NUGROHO
Date Deposited:	21 Feb 2020 09:05
Last Modified:	21 Feb 2020 09:05
URI:	http://eprints.ums.ac.id/id/eprint/81559

Actions (login required)

View Item