Hefridha, Megis and , Ir. Bibit Sugito, MT (2018) Analisis Sifat Mekanik Dan Struktur Mikro Pada Penyambungan Plat Beda Material Alumunium Dan Tembaga Menggunakan Metode Friction Stir Welding. Skripsi thesis, Univerisitas Muhammadiyah Surakarta.
![[img]](http://eprints.ums.ac.id/style/images/fileicons/application_pdf.png) |
PDF (Bab I)
BAB I.pdf Download (230kB) |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (955kB) |
|
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (224kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (5MB) |
|
PDF (Halaman Depan)
HALAMAN DEPAN.pdf Download (1MB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (1MB) |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (1MB) |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (294kB) |
|
PDF (Naskah Publikasi)
NASKAH PUBLIKASI-358 Megis.pdf Download (1MB) |
|
PDF (Surat Pernyataan Publikasi)
publikasi.pdf Download (159kB) |
Abstract
ABSTRACT The purpose of this research is to is so that can know the power of different material welding connection by doing Tensile Test, Vickers Hardness Test, and Micro Structure on FSW welding.Welding on research uses the material of Aluminum series 6011 and Pure Copper with 2 mm thick. The parameters used are 1250 rpm rotational speed , feed rate speed 12.5 mm / minute. Welding results are analyzed by comparing the strength of welded joints between similar materials with different material types.From the results of different material welding testing showed maximum tensile stress of 67,30 MPa and maximum stretch of 4,59 %. For testing the hardness of the welding area there is a significant increase in hardness in the Stir Zone area compared to the HAZ area and the parent metal. The microstructure on the material dissimilar of test results indicates the presence of mixing of both metals in the Stir Zone area , on the HAZ Cu area the grain size decreased compared the grain size HAZ to material similar, whereas on the HAZ Al area has grain size enlargement compared to HAZ of similar material. Keywords: FSW, Aluminum and Copper, Micro Structure, Mechanical Properti.
| Item Type: | Karya ilmiah (Skripsi) |
|---|---|
| Uncontrolled Keywords: | FSW, Aluminum and Copper, Micro Structure, Mechanical Properti. |
| Subjects: | T Technology > T Technology (General) T Technology > TA Engineering (General). Civil engineering (General) |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | MEGIS HEFRIDHA |
| Date Deposited: | 28 May 2018 08:51 |
| Last Modified: | 12 Dec 2018 02:28 |
| URI: | http://eprints.ums.ac.id/id/eprint/62701 |
Actions (login required)
 |
View Item |