Study Pengaruh Hcl 17% Dan 20% Terhadap Kekuatan Bonding Pelapisan Baja Karbon Rendah Menggunakan Kaca Bekas

Izzuddin, Ahmad and , Patna Partono, S.T., M.T. (2018) Study Pengaruh Hcl 17% Dan 20% Terhadap Kekuatan Bonding Pelapisan Baja Karbon Rendah Menggunakan Kaca Bekas. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (227kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (287kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (515kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (99kB)
	PDF (Daftar Pustaka) Daftar Pustaka.pdf Download (99kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (1MB)
	PDF (Pernyataan Publikasi) PERNYATAAN publikasi.pdf Restricted to Repository staff only Download (197kB)
	PDF (Naskah Publikasi) NASKAH PUBLIKASI-238 Ahmad izzudin.pdf Download (914kB)
	PDF (Halaman Depan) HALAMAN DEPAN-175 Ahmd izzudin.pdf Download (720kB)
	PDF (Bab I) BAB I-120 Ahmad Izzuddin.pdf Download (135kB)

Abstract

glass composer and then compare it with chemical composition standard for glass enameling. The study also aims to determine the effect of HCL 17% and 20% on low carbon steel. by looking at micro and adhesion between enamel and low carbon steel surfaces. This study uses SEM (Scanning Electron Microscope) test to determine the chemical composition of the glass. Meanwhile, to know the effect of HCl 17% and 20% on low carbon steel surface, surface roughness testing and micro photo testing were done. To know the result of the tightness of glass coating test which is done that is bonding test which according to European Standard EN10209. Based on the test results can be concluded that the glass that can be used in glass coating is a glass that has a chemical composition close to the standard chemical composition of enamel glass is a low percentage of silica content and a fairly high percentage of alumina and floor. In testing of micro and bond photographs of 17% and 20% HCl effect on low carbon steel surfaces, the best strength of bonding results in the duration of metal immersion in HCl 20% for 30 hours.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	glass coating, low carbon, porstex, strength of bonding, vixal
Subjects:	T Technology > TS Manufactures
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	AHMAD IZZUDDIN
Date Deposited:	12 Apr 2018 01:30
Last Modified:	12 Apr 2018 01:30
URI:	http://eprints.ums.ac.id/id/eprint/62064

Actions (login required)

View Item