Treatment Alumunium 6063 Menggunakan Karbon DiDekoratif Partiker Nikel

Abdillah, Al Munghirah Ibnu and , Masyrukan S.T., M.T. (2024) Treatment Alumunium 6063 Menggunakan Karbon DiDekoratif Partiker Nikel. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASPUB IBNU.pdf Download (2MB)
	PDF (Halaman Depan) HALAMAN DEPAN .pdf Download (3MB)
	PDF (Bab I) BAB I.pdf Download (147kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (347kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (411kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (2MB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (46kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (115kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (2MB)
	PDF (Surat Pernyataan Publikasi) Surat Pernyataan Publikasi_D200190007_Al Munghirah Ibnu Abdillah.pdf Restricted to Repository staff only Download (323kB)

Abstract

This research aims to determine the effect of carbon decorated nickel particles on aluminum 6063 with carburizing treatment. The research process that will be carried out includes several tests, namely Scanning Electron Microscopy (SEM) testing. Scanning Electron Microscopy (SEM) testing was carried out using the ASTM E986 standard. The results of the Scanning Electron Microscopy (SEM) test at stage 1 showed that C and Ni increased and Al decreased, with these results indicating even diffusion on the surface of the specimen. Meanwhile, stage 2 testing showed that C and Al had decreased and Ni had increased, with these results indicating that the depth and spread of diffusion did not reach the core of the specimen.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Aluminum 6063, Carbon Decorative, Carburizing Treatment, Scanning Electron Microscopy
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TN Mining engineering. Metallurgy
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	AL MUNGHIRAH IBNU ABDILLAH
Date Deposited:	25 Jul 2024 01:49
Last Modified:	25 Jul 2024 01:49
URI:	http://eprints.ums.ac.id/id/eprint/125347

Actions (login required)

View Item