Studi Pengecoran Aluminium Dengan Metode Gravity Investment Casting Dan Centrifugal Investment Casting Terhadap Density, Porositas, Struktur Mikro Dan Kekerasan

Utama Putra, Angga Setya and , Patna Partono, S.T., MT. (2022) Studi Pengecoran Aluminium Dengan Metode Gravity Investment Casting Dan Centrifugal Investment Casting Terhadap Density, Porositas, Struktur Mikro Dan Kekerasan. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (1MB)
	PDF (Bab I) BAB I.pdf Download (118kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (798kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (172kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (172kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (449kB)
	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN.pdf Restricted to Repository staff only Download (215kB)

Abstract

This study aims to determine the comparison of gravity investment casting and centrifugal investment casting methods on density, porosity, microstructure and hardness values with aluminum raw materials from used pistons. In this study, two casting methods were used, namely gravity investment casting and centrifugal investment casting with a casting temperature of 750°C. Chemical composition testing using Emission Spectrometry (ASTM E-1251). Observation of porosity was carried out by macro photography using a digital microscope and comparing the results of each variation of the mold temperature. Hardness test using Rockwell hardness tester (ASTM E-384). Testing the microstructure of the castings using a metallographic microscope (ASTM E3-11). The results of the chemical composition test show that this material contains (Al) 71.05%, (Si) 13.65%, (Cu) 7.178%, (Fe) 3.4508%, (Zn) 1.7870% and the elements others up to 100%, according to the ASTM standard B-85 is classified into Aluminum Al-Si (Aluminum – Silicon) A413.0. The results of the calculation of the density of the test object from the gravity investment casting are 2.6764 gr/cm3 and the centrifugal investment casting is 2.6978 gr/cm3. The results of porosity observations that the amount of porosity affects the density value. The results of the observation of the microstructure consist of the phase (Al) and the phase (Si). The beta phase granules (Si) in gravity investment casting appear to be larger and less numerous. In centrifugal investment casting, the beta phase granules are seen to be smaller and more numerous. The size, number and distribution of beta granules affect the hardness value. The results of hardness testing with gravity investment casting have a hardness value of 86.84 HVN, centrifugal investment casting has a hardness value of 98.50 HVN.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	gravity investment casting, centrifugal investment casting, aluminum, porosity, microstructure, hardness
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ANGGA SETYA UTAMA PUTRA
Date Deposited:	13 Feb 2022 12:25
Last Modified:	13 Feb 2022 12:25
URI:	http://eprints.ums.ac.id/id/eprint/97461

Actions (login required)

View Item