Alamsyah, Amril and , Ir. Pramuko Ilmu Purboputro, MT. (2021) Analisa Scanning Electron Microscope (SEM) Hasil Spot Welding Aluminium (Al) dengan Penambahan Serbuk Tembaga (Cu) Mesh 60. Skripsi thesis, Universitas Muhammadiyah Surakarta.
PDF (Naskah Publikasi)
NASKAH PUBLIKASI.pdf Download (1MB) |
|
PDF (Halaman Depan)
HALAMAN DEPAN.pdf Download (1MB) |
|
PDF (Bab I)
BAB I.pdf Download (433kB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (746kB) | Request a copy |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (696kB) | Request a copy |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (1MB) | Request a copy |
|
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (207kB) | Request a copy |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (321kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (2MB) | Request a copy |
|
PDF (Surat Pernyataan Publikasi)
SURAT PERNYATAAN PUBLIKASI ILMIAH.pdf Restricted to Repository staff only Download (181kB) | Request a copy |
Abstract
This study aims to analyze the effect of adding copper mesh 60 powder on spot welded joints using aluminum material. This research conducted 3 tests, namely microstructure, Vickers hardness and SEM-EDX. The results of the microstructure test show that in the base metal area there are large grains, in the HAZ (Heat Affected Zone) area there are smaller grains when compared to the base metal area while in the weld nugget area there are smaller and very dense grains. The results of the Vickers hardness test show that the area that has the highest hardness value is the nugget area, which is 50.14 VHN, then the HAZ (Heat Affected Zone) area is 39.41 VHN, and the lowest is the base metal area, which is 35.36. VHN. The results of the SEM test showed that the copper powder was diffused to the aluminum substrate, the filler was able to fill the empty parts. There are several defects, namely cracks, porosity, and voids. Then the EDX results showed the results of the decreased Al content in the diffusion area due to the content of Cu filler which was able to fill the aluminum area that contained cavities and replace the elements contained in Al. The line analysis indicated several elements, namely Aluminum (Al), Carbon (C), Copper (Cu), and Sodium (Na).
Item Type: | Karya ilmiah (Skripsi) |
---|---|
Uncontrolled Keywords: | Las Titik, Serbuk Tembaga, Uji Mekanik |
Subjects: | T Technology > TJ Mechanical engineering and machinery |
Divisions: | Fakultas Teknik > Teknik Mesin |
Depositing User: | AMRIL ALAMSYAH |
Date Deposited: | 15 Nov 2021 06:23 |
Last Modified: | 15 Nov 2021 06:23 |
URI: | http://eprints.ums.ac.id/id/eprint/95641 |
Actions (login required)
View Item |