Analisa Sifat Fisis Dan Mekanik Cetakan Permanen Dengan Material Besi Cor Ductile Melalui Cetakan Pasir Yang Di-Heat Treatment Dan Tanpa Di-Heat Treatment

Abdillah, Ahmad Faurok and , Agus Yulianto, ST, MT (2021) Analisa Sifat Fisis Dan Mekanik Cetakan Permanen Dengan Material Besi Cor Ductile Melalui Cetakan Pasir Yang Di-Heat Treatment Dan Tanpa Di-Heat Treatment. Skripsi thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
Naskah publikasi.pdf

Download (657kB)
[img] PDF (Bab II)
BAB II.pdf

Download (577kB)
[img] PDF (Bab III)
BAB III.pdf

Download (1MB)
[img] PDF (Bab IV)
BAB IV.pdf

Download (290kB)
[img] PDF (Bab V)
BAB V.pdf
Restricted to Repository staff only

Download (35kB) | Request a copy
[img] PDF (Lampiran)
Lampiran.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf

Download (89kB)
[img] PDF (Surat Pernyataan Publikasi)
Surat Pernyataan Publikasi Karya Ilmiah.pdf
Restricted to Repository staff only

Download (73kB) | Request a copy
[img] PDF (Bab I)
BAB I.pdf

Download (67kB)
[img] PDF (Halaman Depan)
Halaman Dalam.pdf

Download (707kB)

Abstract

The purpose of this work is to investigate effect of the flame hardening process on hardness and wear rate of ferro casting ductile for permanent mold. The process of flame hardening was carried out by heating the edge of the specimen with an oxy-acetylene flame to temperature of 900 oC, and then followed by quenching process on the edge that was burned. The Vickers hardness testing was carried out on specimens with flame hardening and without flame hardening.The hardness was conducted at five points, namely at a distance of 1 mm, 2 mm, 3 mm, 25 mm and 54 mm from the edge. Wear test was conducted by using Abrasive Wear Test. From the results of hardness and wear test,the hardness of specimens without flame hardening at a distance of 1 mm, 2 mm, 3 mm, 25 mm and 54 mm from the edge were 137.3 VHN, 141.1 VHN, 137.3 VHN, 130.1 VHN and 137.3 VHN, respectively.In the wear test, the weight loss for specimens without flame hardening process was 184.3 mg. While for the specimens that were processed by flame hardening, the hardness obtained at a distance of 1 mm, 2 mm, 3 mm, 25 mm and 54 mm from the edge were 328.8 VHN, 249.7 VHNN, 117.4 VHN, 120.4 VHN and 117.4 VHN, respectively. The weight loss specimen with a flame hardening process was 136.3 mg. There were increasing hardness and wear resistance after flame hardening processes.

Item Type: Karya ilmiah (Skripsi)
Uncontrolled Keywords: besi cor ductile, pengeresan api, kekerasan, cetakan permanen, keausan
Subjects: Q Science > Q Science (General)
Q Science > QC Physics
T Technology > TS Manufactures
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: AHMAD FAUROK ABDILLAH
Date Deposited: 25 Sep 2021 04:03
Last Modified: 25 Sep 2021 04:30
URI: http://eprints.ums.ac.id/id/eprint/94458

Actions (login required)

View Item View Item