Wahyu Utomo, Vebra and -, Agung Setyo Darmawan, S.T., M.T. (2021) PENGARUH QUENCHING DAN TEMPERING PADA TEMPERATUR 650°C TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KETANGGUHAN PADA BESI COR NODULAR. Skripsi thesis, Universitas Muhammadiyah Surakarta.
PDF (Naskah Publikasi)
NASKAH PUBLIKASI.pdf Download (1MB) |
|
PDF (Halaman Depan)
HALAMAN DEPAN.pdf Download (1MB) |
|
PDF (Bab I)
BAB I .pdf Download (174kB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (1MB) | Request a copy |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (741kB) | Request a copy |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (956kB) | Request a copy |
|
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (241kB) | Request a copy |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (166kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (2MB) | Request a copy |
|
PDF (Surat Pernyataan Publikasi)
SURAT PERNYATAAN PUBLIKASI ILMIAH.pdf Restricted to Repository staff only Download (262kB) | Request a copy |
Abstract
This research was conducted to determine the effect of quenching and tempering treatment on microstructure, hardness and toughness of nodular cast iron material. The quenching treatment process with a temperature of 850ºC for 30 minutes cooling water media and continued tempering with a temperature of 650ºC held for 60 minutes cooling room temperature. In the SEM microstructure test on the quenching material, the martensite phase appears, after the tempering process the martensite phase changes to the tempered martensite phase which has toughness but lower hardness than the martensite phase. So that the results of the Rockwell hardness test with quenching treatment experienced an increase in hardness of 56.73 HRC after tempering treatment decreased by 21.33 HRC from the hardness of raw material 24.33 HRC. The results of the impact test of the Charpy method on the quenching material, the toughness value decreased by 0.068 (J/mm²) the impact price. After tempering it increases with an impact energy of 0.097 (J/mm²).
Item Type: | Karya ilmiah (Skripsi) |
---|---|
Uncontrolled Keywords: | nodular cast iron, quenching, tempering, SEM, hardness, toughness |
Subjects: | T Technology > TJ Mechanical engineering and machinery |
Divisions: | Fakultas Teknik > Teknik Mesin |
Depositing User: | VEBRA WAHYU UTOMO |
Date Deposited: | 14 Aug 2021 04:28 |
Last Modified: | 14 Aug 2021 04:28 |
URI: | http://eprints.ums.ac.id/id/eprint/93258 |
Actions (login required)
View Item |