Mustika, Aan candra and , Agus Yulianto, ST, MT (2021) Karakterisasi Besi Cor Kelabu dengan Penambahan FeMn 3% Berat pada Proses Pengecoran dengan Cetakan Logam dan dCetakan Pasir. Skripsi thesis, Universitas Muhammadiyah Surakarta.
PDF (Naskah Publikasi)
NASKAH PUBLIKASI.pdf Download (1MB) |
|
PDF (Halaman Depan)
Halaman Depan.pdf Download (1MB) |
|
PDF (Bab I)
BAB I.pdf Download (306kB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (608kB) | Request a copy |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (1MB) | Request a copy |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (1MB) | Request a copy |
|
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (191kB) | Request a copy |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (405kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (1MB) | Request a copy |
|
PDF (Surat Pernyataan Publikasi)
pernyataan publikasi AAN.pdf Restricted to Repository staff only Download (219kB) | Request a copy |
Abstract
This study aims to find out how the effect of manganese element inoculation (FeMn) on hardness values, microstructure photos and SEM EDS test results on gray cast iron material with the addition of FeMn 3%. In this casting process using induction smelting furnace with a temperature of 1300 - 1400 C material used for smelting ie iron (Fe), iron melted then mixed with FeMn 3% after mixing poured into the mold of metal and sand that has been prepared. Hardness test results showed the hardness value of the upper metal mold result of 215 BHN of the middle metal mold of 257 BHN, the lower metal mold of 334 BHN. The hardness value of the upper transition mold is 214 BHN, the middle transition mold is 251 BHN, the lower transition mold is 326 BHN. The hardness value of the upper sand mold is 187 BHN, the middle sand mold is 209 BHN, the bottom sand mold is 229 BHN. Microstructure test results from metal molds, transition molds, sand molds at the bottom are hardest because graphite is neatly arranged and clearly visible. Sem EDS Mn element test results on metal mold results were detected by 3.45% and at 0.00% sand mold, on Mn sand mold results were actually detected on the chart but did not appear on the data table because it was covered by Fe, C, and Si elements.
Item Type: | Karya ilmiah (Skripsi) |
---|---|
Uncontrolled Keywords: | Manganese (FeMn), MicroStructure Test, Hardness Test, SEM EDS Test |
Subjects: | T Technology > TJ Mechanical engineering and machinery T Technology > TS Manufactures |
Divisions: | Fakultas Teknik > Teknik Mesin |
Depositing User: | A'AN CANDRA MUSTIKA |
Date Deposited: | 16 Aug 2021 03:12 |
Last Modified: | 16 Aug 2021 03:12 |
URI: | http://eprints.ums.ac.id/id/eprint/92596 |
Actions (login required)
View Item |