Studi Sifat Mekanis Las Brazing dengan Penyambungan Lap Joint Pada Material Aluminium, Kuningan dan Tembaga

Hanafi, Aziz and , Joko Sedyono, ST, M.Eng, Ph.D (2018) Studi Sifat Mekanis Las Brazing dengan Penyambungan Lap Joint Pada Material Aluminium, Kuningan dan Tembaga. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) Naspub.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (1MB)
	PDF (Bab I) BAB I.pdf Download (168kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (687kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (89kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (9kB)
	PDF (Lampiran) Lampiran.pdf Restricted to Repository staff only Download (5MB)
	PDF (Surat Pernyataan Publikasi) Surat Publikasi.pdf Restricted to Repository staff only Download (115kB)

Abstract

This research was conducted to know the mechanical properties of aluminum, brass and copper material by using brazing welding by using lap joint method. In this research the method used for this testing process is chemical composition test, micro photo test, and tensile test. The basic material used is aluminum plate, brass, and copper which is then welded brazing by joint lap joint method. Based on the research that has been done, the authors have obtained the test results. In the composition test made aluminum material contains some of the highest composition of Aluminum (Al) 97.41%, for brass material contains some composition that is copper (Cu) 64.2%, Zinc (Zn) 34.8%, while copper containing copper composition (Cu) 98.3%. At the tensile test conducted the higest strenght of brass with a value of 281,335 Mpa, The results of micro-photos obtained on Aluminium, Brass and Copper meterials have not changed the microstructure because the etching process has not been perfect, resulting in a micro photo test process that does not look at the micostructure.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	Aluminium, Kuningan, Tembaga, Lap Joint, Las Brazing Kuningan, Uji Komposisi, Uji Tarik, Uji Foto Mikro
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	AZIZ HANAFI
Date Deposited:	13 Nov 2018 03:06
Last Modified:	13 Nov 2018 03:06
URI:	http://eprints.ums.ac.id/id/eprint/68857

Actions (login required)

View Item