Suprobo, Danasmoro Dyah and , drg. Noor Hafida Widyastuti, Sp.KG (2018) Perbandingan Kekuatan Tekan Resin Komposit Nanofill Dengan Polimerisasi Sinar Light-Curing Menggunakan Teknik Ramped Dan Pulse Delay. Skripsi thesis, Universitas Muhammadiyah Surakarta.
PDF (Naskah Publikasi)
NASKAH PUBLIKASI.pdf Download (530kB) |
|
PDF (Halaman Depan)
HALAMAN DEPAN.pdf Download (592kB) |
|
PDF (Bab I)
BAB I.pdf Download (160kB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (277kB) | Request a copy |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (174kB) | Request a copy |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (140kB) | Request a copy |
|
PDF (Bab V)
BAB v.pdf Restricted to Repository staff only Download (83kB) | Request a copy |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (205kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (532kB) | Request a copy |
|
PDF (Pernyataan Publikasi)
PERNYATAAN PUBLIKASI.pdf Restricted to Repository staff only Download (187kB) | Request a copy |
Abstract
Nanofil have small particles with an average size of 0.2-0.1 μm. The polymerization of the composite resin utilizes a radical group obtained by light-cured composite or a self-cured composite. The irradiation technique is ramped and pulse delay.The purpose of this research is to know comparative strength ratio of nanofil composite resin with different ray polymerization between ramped and pluse-delay irradiation.Motion used by means All research subjects measured compressive strength using Universal Testing Machine (UTM) with a maximum load of 20kg. Measurement of compressive strength is done by placing the object of research on the fixation tool located at the center of the machine. The engine is turned on until it moves upwards at a speed of 0.5 mm / min until the object is fractured.The results showed the average value and standard deviation of composite resin compressive strength in group I of 16 and 174,581 ± 7,848 in group II of 16 and 185,634 ± 8,438. The result of independent t-test of composite nanofil resin compressive strength on ramped and pulse delay technique is 0,001 so that p> 0,05 so it can be concluded that there is significant difference between ramped irradiation and pulse delay to strength test where pulse delay compression value is greater than Radiation ramped.
Item Type: | Karya ilmiah (Skripsi) |
---|---|
Uncontrolled Keywords: | nanofil, compressive strength, ramped, pulse delay |
Subjects: | R Medicine > R Medicine (General) |
Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
Depositing User: | DANASMORO DYAH SUPROBO |
Date Deposited: | 07 Aug 2018 08:43 |
Last Modified: | 07 Aug 2018 08:43 |
URI: | http://eprints.ums.ac.id/id/eprint/65437 |
Actions (login required)
View Item |