Study Pengaruh HCl Terhadap Kekuatan Bonding Pelapisan Besi Cor Kelabu Menggunakan Kaca Bekas dengan Jenis Amplas 220 Dan 400

Budiyarto, Wahyu and -, Patna Partono, S.T., M.T. (2018) Study Pengaruh HCl Terhadap Kekuatan Bonding Pelapisan Besi Cor Kelabu Menggunakan Kaca Bekas dengan Jenis Amplas 220 Dan 400. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) Naskah Publikasi.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (863kB)
	PDF (Bab I) BAB I.pdf Download (111kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (266kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (286kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (902kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (98kB)
	PDF (Daftar Pustaka) Daftar Pustaka.pdf Download (60kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (1MB)
	PDF (Pernyataan Publikasi) PERNYATAAN PUBLIKASI.pdf Restricted to Repository staff only Download (502kB)

Abstract

This study aims to determine the chemical composition of glass compilers and then compared with the standard chemical composition for glass enameling. This study also aims to determine the effect of HCL on gray cast iron, by looking at micro and adhesion between enamel and low carbon steel surface. This study uses SEM (Scaning Electron Microscope) test to determine the chemical composition of glass. Meanwhile, to determine the effect of HCL on the surface of gray cast iron was done surface roughness testing and micro photo testing. To know the result of tightness of glass coating is done bonding test in accordance with European Standard EN10209. Based on the test results can be concluded that, glass that can be used in glass coating is a glass that has a chemical composition close to the standard chemical composition of enamel glass, which has a low content of silica percentage and the percentage of alumina and floor is quite high. In testing of micro and bond photographs of HCL effect on gray cast iron surface, the best strength of bonding results in the duration of metal immersion in HCl fluid with type of sandpaper 220 for 30 hours.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	gray cast iron, glass coating, strength of bonding
Subjects:	T Technology > TS Manufactures
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	WAHYU BUDIYARTO
Date Deposited:	20 Jul 2018 09:44
Last Modified:	20 Jul 2018 09:44
URI:	http://eprints.ums.ac.id/id/eprint/63694

Actions (login required)

View Item