Ananda, Yeda Febry and , Ir. Suhendro Trinugroho, M.T (2017) Pengaruh Waktu Campur Dan Faktor Air Semen Terhadap Kuat Tekan Dan Kuat Tarik Belah Beton 1 Hari Dengan Bahan Tambah Fly Ash Abu Limbah Batu Bara. Diploma thesis, Universitas Muhammadiyah Surakarta.
![]() |
PDF (NASKAH PUBLIKASI)
NASKAH PUBLIKASI.pdf Download (1MB) |
![]() |
PDF (HALAMAN DEPAN)
HALAMAN DEPAN.pdf Download (1MB) |
![]() |
PDF (BAB I)
BAB I.pdf Download (168kB) |
![]() |
PDF (BAB II)
BAB II.pdf Restricted to Repository staff only Download (193kB) |
![]() |
PDF (BAB III)
BAB III.pdf Restricted to Repository staff only Download (147kB) |
![]() |
PDF (BAB IV)
BAB IV.pdf Restricted to Repository staff only Download (1MB) |
![]() |
PDF (BAB V)
BAB V.pdf Restricted to Repository staff only Download (312kB) |
![]() |
PDF (BAB VI)
BAB VI.pdf Restricted to Repository staff only Download (143kB) |
![]() |
PDF (DAFTAR PUSTAKA)
DAFTAR PUSTAKA.pdf Download (134kB) |
![]() |
PDF (LAMPIRAN)
LAMPIRAN.pdf Restricted to Repository staff only Download (1MB) |
![]() |
PDF (PERNYATAAN KARYA ILMIAH)
surat pernyataan artikel publikasi.pdf Restricted to Repository staff only Download (186kB) |
Abstract
Concrete is a composite material (mixture) of several materials, the material consisting essentially of a mixture of cement, fine aggregate, coarse aggregate, water and other additives by comparison.Today coal waste often gets the spotlight, because it can cause carbon dioxide gas tha t is harmful to the environment. With various co nsiderations then developed the material as a binder for the manufacture of concrete. One of the materials used is ash waste coal (fly ash) . By utilizing fly ash as an added material for the manufacture of concrete is considered to reduce emissions of carb on dioxide gas in the air . In this study the specimens used were cylinders, with a diameter of 15cm and a height of 30cm. Tensile and compressive strength tests were performed on concrete days 1 day and 28 days. The variations on the test include the cemen t water factor of 0.3, 0.35 and 0.4 and the mixing mixture variation of concrete at 5; 7.5 and 10 minutes. In the concrete test, the highest compressive strength and tensile strength of the concrete were mixed with 7.5 minute mixed time and 0.35 for the fa s. So it can be concluded that the highest mixing time of concrete mixture is 7.5 minutes with the cement water ratio of 0.35. If less than 7.5 minutes result in less binder binder. And when mixing time more than 7.5 minutes resulted in the binder's declin ing power. This results in the compressive strength of the concrete at the time the test is decreased. So also with the use of cement water ratio, the best variation is 0,3 5 with a compressive strength value of 17.8344 MPa (1 day), 32.4605 MPa ( 28 days) an d a value of 1.7929 MP a (1 day), 3.2083 MPa ( 28 days). Keywords: early age concrete,flyash,cement water ratio,mixing time
Item Type: | Karya ilmiah (Diploma) |
---|---|
Uncontrolled Keywords: | beton 1 hari, fly ash, fas, waktu pencampuran. |
Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
Divisions: | Fakultas Teknik > Teknik Sipil |
Depositing User: | YEDA FEBRY ANANDA |
Date Deposited: | 25 Oct 2017 06:06 |
Last Modified: | 25 Oct 2017 06:06 |
URI: | http://eprints.ums.ac.id/id/eprint/56482 |
Actions (login required)
![]() |
View Item |