Perencanaan Dan Pembuatan Produk Untuk Cetakan Permanen Dengan Material Fcd Menggunakan Cetakan Pasir Co2

Ahsani, Arif and , Patna Partono, ST, MT (2017) Perencanaan Dan Pembuatan Produk Untuk Cetakan Permanen Dengan Material Fcd Menggunakan Cetakan Pasir Co2. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI-libraryums-Arif.pdf Download (1MB)
	PDF (Halaman Depan) Halaman Depan.pdf Download (1MB)
	PDF (BAB I) BAB 1.pdf Download (96kB)
	PDF (BAB II) BAB 2.pdf Restricted to Repository staff only Download (834kB) | Request a copy
	PDF (BAB III) BAB 3.pdf Restricted to Repository staff only Download (1MB) | Request a copy
	PDF (BAB IV) BAB 4.pdf Restricted to Repository staff only Download (899kB) | Request a copy
	PDF (BAB V) BAB 5.pdf Restricted to Repository staff only Download (89kB) | Request a copy
	PDF (Daftar Pustka) DAFTAR PUSTAKA.pdf Download (178kB)
	PDF (Lampiran) lampiran.pdf Restricted to Repository staff only Download (726kB) | Request a copy
	PDF (Surat Pernyataan Publikasi Ilmiah) pernyataan tiwul.pdf Restricted to Repository staff only Download (570kB) | Request a copy

Abstract

Metal moulding is part of first industrial in manufakture field, consist of iron melted process and then liquid of metal dicorkan into space of mould and in the solidification until it froze. Cast iron FCD/dutile is made by by enchancing a few magnesium element, addition of this element it coused form cast iron graphite become FCD/ductile, or circule. Transformation of this grphite is following with resilient charge, so resilient of cast iron is increased. Hence of that, FCD cast iron is called resilient cast iron where the resilient is among 10%-20%. Sand casting is represent of dry sand printed mould caused rated of water in the printing mould is little. For that related research is very needed to planning and making of produck for permanet mould with material cast iron FCD/ductile, using sand casting CO2. Based of channel system calculation at under mould can resulted the value of gating system 3,91339 cm2, sprue with comparation formula 1:1 3,91339 cm2, high of infusion 10,966 cm, and decreased value 79.565,625 mm3. And undercarriage printed, in gating system 4,15368 cm2, sprue with comparation formula 1:1 4,15368 cm2, high of infusion 4,69 cm, and decreased value 37.130,625 mm3.

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	Metal Casting, cast iron ductile,sand casting, system pathen
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ARIF AHSANI
Date Deposited:	02 Aug 2017 06:04
Last Modified:	02 Aug 2017 06:05
URI:	http://eprints.ums.ac.id/id/eprint/54116

Actions (login required)

View Item