Analisis Kekuatan Tarik Dan Struktur Mikro Pada Sambungan T-Joint Dan Butt Joint Pipa Alumunium Dengan Metode Soldering

Martanto, Prihatin Iwan and , Agus Dwi Anggono, ST, M.Eng, Ph.D (2017) Analisis Kekuatan Tarik Dan Struktur Mikro Pada Sambungan T-Joint Dan Butt Joint Pipa Alumunium Dengan Metode Soldering. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) naskah publikasi-72.pdf Download (1MB)
	PDF (Halaman Depan) halaman depan.pdf Download (1MB)
	PDF (Bab I) BAB I.pdf Restricted to Repository staff only Download (107kB) | Request a copy
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (730kB) | Request a copy
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (486kB) | Request a copy
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (1MB) | Request a copy
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (99kB) | Request a copy
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (204kB)
	PDF (Lampiran) lampiran 2 fix.pdf Restricted to Repository staff only Download (2MB) | Request a copy
	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN.pdf Download (21kB)

Abstract

Soldering method have been used to joint aluminium pipe to increase the efectiveness and eficiency in the product creation due to aluminiun was a hard-to weld material. This research objective is to joint aluminium pipe of 16 mm diameters and 1 mm thickness by using soldering method with alusol filler. Joinning strength of soldering will be investigated as well. There are two types of joinning i.e butt joint and T-joint. Analysis was conducted by using tensile test and photo micro to investigate the material structure. Tensile test standard was adopted ASTM E8M and ASTM E3 for photo micro. The soldering result shows the breaking area of soldering zone. The tensile test of T-joint was given the tensile value of 10.959 N/mm2 and the strain walue was 3.93%. Tensile test of butt joint was delivered stress of 3.124 N/mm2 and strain of 3.9%. The micro structure of HAZ was shown smaller grain due to the heat effect to the aluminium, and also in the soldering zone of filler material. It was seen smaller grain size compare to the base aluminium

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	soldering, aluminum pipe, filler alusol
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	PRIHATIN IWAN MARTANTO
Date Deposited:	20 Apr 2017 10:33
Last Modified:	20 Nov 2019 01:37
URI:	http://eprints.ums.ac.id/id/eprint/52203

Actions (login required)

View Item