Analisis Sifat Mekanis Beton Mutu Tinggi dengan Memanfaatkan Teknologi High Volume Fly Ash Concrete

Prihantoro, Teguh Fajar and , Mochamad Solikin, S.T., M.T., Ph.D and , Budi Setiawan, S.T., M.T (2015) Analisis Sifat Mekanis Beton Mutu Tinggi dengan Memanfaatkan Teknologi High Volume Fly Ash Concrete. Diploma thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (NASKAH PUBLIKASI)
NASKAH PUBLIKASI.pdf

Download (591kB)
[img] PDF (HALAMAN DEPAN)
HALAMAN DEPAN.pdf

Download (385kB)
[img] PDF (BAB I)
BAB I.pdf

Download (206kB)
[img] PDF (BAB II)
BAB II .pdf
Restricted to Repository staff only

Download (138kB)
[img] PDF (BAB III)
BAB III .pdf
Restricted to Repository staff only

Download (518kB)
[img] PDF (BAB IV)
BAB IV .pdf
Restricted to Repository staff only

Download (765kB)
[img] PDF (BAB V)
BAB V .pdf
Restricted to Repository staff only

Download (570kB)
[img] PDF (BAB VI)
BAB VI .pdf
Restricted to Repository staff only

Download (91kB)
[img] PDF (DAFTAR PUSTAKA)
DAFTAR PUSTAKA.pdf

Download (193kB)
[img] PDF (LAMPIRAN)
lampiran.pdf
Restricted to Repository staff only

Download (1MB)
[img] PDF (PERNYATAAN PUBLIKASI ILMIAH)
Surat Pernyataan Publikasi.pdf
Restricted to Repository staff only

Download (118kB)

Abstract

Concrete technology over time increasingly experiencing growth, this is done to improve the quality of the concrete is to obtain a high strength and durability. This study aimed to obtain a high quality concrete by using fly ash as a cement material to replace up to 50% (high volume fly ash concrete). This research was conducted by examining the development of compressive strength of concrete high volome fly ash at the age of 14 days, 28 days and 56 days, testing the flexural strength of concrete high volome fly ash at the age of 56 days, to test the value of the modulus of elasticity of concrete high volome fly ash at the age of 56 days and test the water absorption value volome high fly ash concrete at the age of 56 days, as well as a comparison that is testing without a mixture of fly ash concrete (normal concrete). Both mixtures using fas low that using superplasticizer 1 % to achieve good workability upon mixing. The planned strength of concrete is 45 MPa using ACI with a slump value of ± 10 cm. From this study showed that the compressive strength of normal concrete and concrete HVFA respectively at the age of 14 days amounted to: 37.9 MPa and 28.8 MPa, at 28 days amounted to: 39.9 MPa and 39.4 MPa, and at the age of 56 days amounted to: 41.6 MPa and 42.5 MPa. The test results for the flexural strength of normal concrete and concrete HVFA each is 8.8 MPa and 8.6 MPa. Results of testing the modulus of elasticity of concrete for normal concrete and concrete HVFA each is 34108 MPa and 37 726 MPa. The test results of water absorption of concrete for normal concrete water absorption up to 1.745% and for concrete HVFA water absorption up to 1,431%. From these data indicate compressive strength and flexural strength of concrete HVFA has a value which is comparable to normal concrete, the modulus of elasticity of concrete HVFA larger than normal concrete and concrete water catchment HVFA smaller than normal concrete.

Item Type: Karya ilmiah (Diploma)
Uncontrolled Keywords: beton mutu tinggi; high volume fly ash concrete; sifat mekanis beton; superplasticizer
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Fakultas Teknik > Teknik Sipil
Depositing User: TEGUH FAJAR PRIHANTORO
Date Deposited: 26 Oct 2015 12:18
Last Modified: 12 Oct 2021 22:47
URI: http://eprints.ums.ac.id/id/eprint/38196

Actions (login required)

View Item View Item