Pengaruh Komposisi Kompon Ban Dengan Batikan Zig - Zag Terhadap Koefisien Grip Ban Pada Lintasan Beton Kondisi Basah Dan Kering

Arvianto, Muhamad Wijang and , Ir. Pramuko Ilmu Purbo Putro, MT. and , Wijianto,S.T.,M.Eng.Sc. (2015) Pengaruh Komposisi Kompon Ban Dengan Batikan Zig - Zag Terhadap Koefisien Grip Ban Pada Lintasan Beton Kondisi Basah Dan Kering. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) 11. NASKAH PUBLIKASI.pdf Download (1MB)
	PDF (Halaman Depan) 2. HALAMAN DEPAN.pdf Download (1MB)
	PDF (Bab I) 3. BAB I.pdf Download (153kB)
	PDF (Bab II) 4. BAB II.pdf Restricted to Repository staff only Download (620kB)
	PDF (Bab III) 5. BAB III.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab IV) 6. BAB IV.pdf Restricted to Repository staff only Download (884kB)
	PDF (Bab V) 7. BAB V.pdf Restricted to Repository staff only Download (142kB)
	PDF (Daftar Pustaka) 8. DAFTAR PUSTAKA.pdf Download (86kB)
	PDF (Lampiran) 9. LAMPIRAN.pdf Restricted to Repository staff only Download (11MB)
	PDF (Pernyataan Publikasi Ilmiah) 1. SURAT PERNYATAAN PUBLIKASI KARYA ILMIAH.pdf Restricted to Repository staff only Download (286kB)

Abstract

this research aims to know the influence of the composition of compound tires with batikan zig zag – against the tire grip coefficient on the trajectory of the concrete conditions of wet and dry. Composition varied in the manufacture of compounds, namely carbon black and sulfur. The process of making compounds beginning with the preparation of materials to be used, is 10 compositions used are: Rubber Smoke Sheet (RSS), Styrene Butadiene Rubber (SBR), Carbon black, Parafinic Oil, Zinc Oxide (Zno), Stearic Acid (SA), Paraffin Wax, Dibenzothiazly disulfide (MBTS), Cumaron Resin, Sulfur. After that mix all the materials have been prepared. Further compounds the already so with temperature and time of vulcanization presses. Specimen testing does is test of hardness and hardness test with standard SNI 07778:2009, test the grip with the standard ASTM D2047-99. From the results of the test showed that the value of the highest violence at the compound 3. The results of the tensile test of thermal compound manufacturer has a value of voltage drop, from artificial compound thermal compound 1 has a voltage drop the most approaching the compound manufacturer. Then from the results of the test compound grip manufacturer that has the most grip coefficient values are high, but the wear and tear is high, while the compound 3 has a grip coefficient values are low, but the value of low wear and tear. Keywords: compounds, carbon black, sulfur

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	compounds, carbon black, sulfur
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TL Motor vehicles. Aeronautics. Astronautics
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Muhamad Wijang Arvianto
Date Deposited:	29 Jul 2015 02:40
Last Modified:	13 Oct 2021 01:36
URI:	http://eprints.ums.ac.id/id/eprint/35135

Actions (login required)

View Item