Treatment Aluminium 6063 Menggunakan Karbon Didekoratif Partikel Chrome

Setyoko, Muhammad Daffa and , Masyrukan S.T., M.T. (2024) Treatment Aluminium 6063 Menggunakan Karbon Didekoratif Partikel Chrome. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI DAFFA.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN DEPAN FIX.pdf Download (1MB)
	PDF (Bab-1) BAB I.pdf Download (118kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (272kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (313kB)
	PDF (Bab-IV) BAB IV.pdf Restricted to Repository staff only Download (1MB)
	PDF (Bab-V) BAB V.pdf Restricted to Repository staff only Download (46kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (177kB)
	PDF (Lampiran) LAMPIRAN.pdf Restricted to Repository staff only Download (3MB)
	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN PUBLIKASI.pdf Restricted to Repository staff only Download (330kB)

Abstract

Aluminum has been widely used in recent years to meet increasingly complex needs. Aluminum is a non-ferrous metal that has many advantages and can be applied in almost all fields, so the aluminum industry has products that are widely used in society. This is also supported because aluminum alloys are resistant to corrosion and have high ductility. This research aims to determine the treatment of Aluminum 6063 using carbon decorated with chrome particles. Scanning Electron Microscopy (SEM) testing was carried out using ASTM E98. In testing stages 1 and 2, there was an increase in the value of carbon content and a decrease in the value of aluminum content in all test areas, while the value of chrome particle content tended to be constant or stable. Then the highest carbon content value was found in the stage 2 specimen in the side area after etching with a weight of 71.867%, while the lowest carbon content value was found in the stage 1 specimen in the middle area after etching with a weight of 1.971%, then for the chrome particle value the highest result was obtained in the stage 1 testing on the side area before etching with a weight of 0.198%. Meanwhile, for the chrome particle value, the lowest result was obtained in the phase 1 testing section on the side area after etching with a weight of 0.045%.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Aluminum 6063, Carburizing, Heat Treatment, Carbon, SEM Test
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TN Mining engineering. Metallurgy
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	MUHAMMAD DAFFA SETYOKO
Date Deposited:	25 Jul 2024 02:04
Last Modified:	25 Jul 2024 02:04
URI:	http://eprints.ums.ac.id/id/eprint/125224