Pengelasan Gesek Dengan Variasi Laju Kecepatan Putar Pada Material Baja AISI 1010 Terhadap Kekuatan Sambungan

Firmansyah, Zakaria Tito and , Ir. Bibit Sugito,M.T (2022) Pengelasan Gesek Dengan Variasi Laju Kecepatan Putar Pada Material Baja AISI 1010 Terhadap Kekuatan Sambungan. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) Naskah Publikasi_D200180226.pdf Download (1MB)
	PDF (Halaman Depan) hal depan.pdf Download (1MB)
	PDF (Bab I) Bab 1.pdf Restricted to Repository staff only Download (528kB)
	PDF (Bab II) bab ii new.pdf Restricted to Repository staff only Download (860kB)
	PDF (Bab III) Bab III.pdf Restricted to Repository staff only Download (434kB)
	PDF (Bab IV) Bab IV.pdf Restricted to Repository staff only Download (571kB)
	PDF (Bab V) Bab V.pdf Restricted to Repository staff only Download (224kB)
	PDF (Daftar Pustaka) Daftar Pustaka.pdf Download (342kB)
	PDF (Lampiran) bismillah fix15-71-80.pdf Restricted to Repository staff only Download (510kB)
	PDF (Surat Pernyataan Publikasi) 202211081816461000.pdf Restricted to Repository staff only Download (189kB)

Abstract

This study aims to determine the effect of rotational speed on the joint strength of AISI 1010 steel material, this research was carried out experimentally with variations in rotational speed on friction welding machines, there are three variations in this research 800,1000,1200 RPm. In this study, there are three tests to validate the experimental results that have been carried out, the first is tensile testing, hardness testing and microstructure testing. In this study, it was found that the joining of similar steels with type AISI 1010 which is a low carbon steel produces a flush that is not neatly formed due to centrifugal force during friction welding. For the results of the Tensile Test, the highest tensile strength value is found at 1000 rpm with a value of 716 N/mm2. In addition, the hardness value of the Hardness test in the highest weld area is also found at 1000 rpm . rotation

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Friction welding, Strength of Welding joints, Low Carbon Steel
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ZAKARIA TITO FIRMANSYAH
Date Deposited:	11 Nov 2022 06:36
Last Modified:	11 Nov 2022 06:36
URI:	http://eprints.ums.ac.id/id/eprint/105527

Actions (login required)

View Item