Pengaruh Proses Annealing Terhadap Lapisan Diamond Like Carbon Hasil Proses Plasma Chemical Vapour Deposition Pada Baja AISI 410

Al Hujjaz, M. Syahrul Maulana and , Ir. Agung Setyo Darmawan, S.T., M.T (2022) Pengaruh Proses Annealing Terhadap Lapisan Diamond Like Carbon Hasil Proses Plasma Chemical Vapour Deposition Pada Baja AISI 410. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI ILMIAH.pdf Download (917kB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (1MB)
	PDF (Bab I) BAB I.pdf Download (84kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (405kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (323kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (277kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (9kB)
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (76kB)
	PDF (Lampiran) LAMPIRAN.pdf Download (1MB)
	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN PUBLIKASI ILMIAH.pdf Download (381kB)

Abstract

This study aims to determine the effect of annealing process on the structure and hardness of Diamond Like Carbon (DLC) layer resulting from Plasma Chemical Vapour Deposition (PCVD) process on AISI 410 stainless steel material. The annealing process was carried out on AISI 410 stainless steel material at temperature 850°C with holding time 20 minutes and cooled to room temperature. Furthemore, the process of forming DLC layer was carried out using PCVD method using argon gas and LPG with flow rate ratio 9:1 at pressure 1,6 mbar, temperature 400°C, and coating time 4 hours. The results of Raman Spectroscopy test showed that DLC layer structure on AISI 410 stainless steel which was not annealed had more sp3 (diamond) content than DLC layer on AISI 410 stainless steel which was annealed. The results of Vickers microhardness test showed that DLC layer on AISI 410 stainless steel which was not annealed had a greater hardness value of 914,14 VHN compared to DLC layer on AISI 410 stainless steel which was annealed which was 612,30 VHN.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	Diamond Like Carbon, Baja AISI 410, PCVD, Raman Spectroscopy, Vickers
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	M. SYAHRUL MAULANA AL HUJJAZ
Date Deposited:	06 Aug 2022 06:57
Last Modified:	06 Aug 2022 06:57
URI:	http://eprints.ums.ac.id/id/eprint/102632