Analisa Pengaruh Media Pendingin Heat Treatment terhadap Konduktvitas Thermal pada Alumunium Alloy

Ramadhan, Galih and , Amin Sulistyanto S.T, M.T (2020) Analisa Pengaruh Media Pendingin Heat Treatment terhadap Konduktvitas Thermal pada Alumunium Alloy. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) naskah.pdf Download (1MB)
	PDF (Halaman Depan) HALAMAN.pdf Download (1MB)
	PDF (Bab I) BAB 1.pdf Download (148kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (571kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (432kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (521kB)
	PDF (Bab V) Bab V.pdf Restricted to Repository staff only Download (90kB)
	PDF (Daftar Pustaka) DAFTAR PUSTKA.pdf Download (133kB)
	PDF (Lampiran) LAMPIRRAN.pdf Restricted to Repository staff only Download (561kB)
	PDF (Surat Pernyataan Publikasi) surat pernyataan.PDF Restricted to Repository staff only Download (55kB)

Abstract

This study aims to determine the results of micro-photo testing and the value of thermal conductivity of aluminum alloy with the influence of heat treatment using the media. The process of making aluminum specimens was cut 4mm thick and 6mm thick as many as 4 pieces of heat treated at a temperature of 400 ° C for 30 minutes and cooled using air, water and oil cooling media. After the aluminum heat treatment process then the micro-photo test and thermal conductivity test. The results of the study indicate that aluminum which is heat treated using oilcooling media has the highest thermal conductivity value, and aluminum with aircooling media has the smallest value of thermal conductivity. Keywords: Aluminum alloy, Heat Treatment, Micro Structure, Thermal Conductivity

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	Keywords: Aluminum alloy, Heat Treatment, Micro Structure, Thermal Conductivity
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	GALIH RAMADHAN
Date Deposited:	14 Feb 2020 06:05
Last Modified:	14 Feb 2020 06:05
URI:	http://eprints.ums.ac.id/id/eprint/80859