Karakterisasi Partikel Arang Kayu Bengkirai Hasil Tumbukan High Energy Ball Milling (HEBM) Dan Pemanasan Lanjut Dengan Suhu 300° C

Kusuma, Danar wijaya and , Supriyono, ST, MT, Ph.D (2020) Karakterisasi Partikel Arang Kayu Bengkirai Hasil Tumbukan High Energy Ball Milling (HEBM) Dan Pemanasan Lanjut Dengan Suhu 300° C. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Halaman Depan) Halaman Depan.pdf Download (585kB)
	PDF (Bab I) BAB I.pdf Download (107kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (218kB)
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (602kB)
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (809kB)
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (41kB)
	PDF (Daftar Pustaka) daftar Pustaka.pdf Download (86kB)
	PDF (Surat Pernyataan Publikasi) surat pernyataan publikasi.pdf Restricted to Repository staff only Download (167kB)
	PDF (Lampiran) lampiran.pdf Restricted to Repository staff only Download (999kB)
	PDF (Naskah publikasi) naskah publikasi .pdf Download (1MB)

Abstract

The purpose of this study is to characterize the bengkirai charcoal particles from the collision of the High Energy Ball Milling (HEBM) Machine and further heating, In this study a study of Bengkirai wood charcoal particles produced from an incomplete combustion process and using the collision method with a shaker mills model. Characteristics of particles with the PSA test, SEM test and EDX test to analyze carbon particle size, surface morphology and chemical composition contained in the collision material. The results of the PSA test, at 2.5 million cycles produced an average size of 17, 656 µm, the volume was 11.132%; the smallest size is 1.537 µm, the volume is 0.001%; the largest size is 174,110 µm, the volume is 0.001%. While the SEM test results on cycles of 2.5 million cycles produce carbon particle size that is small and large. The EDX test results in elements that produce carbon particle sizes, C 99.25, Calcium Oxide, CaO 0.16%, Copper (II) Oxide, CuO 0.59% Keywords: characterization, cycle, Bengkirai charcoal, PSA and SEM-EDX

Item Type:	Karya ilmiah (Skripsi)
Uncontrolled Keywords:	Keywords: characterization, cycle, Bengkirai charcoal, PSA and SEM-EDX
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Depositing User:	DANAR WIJAYA KUSUMA
Date Deposited:	14 Aug 2020 03:24
Last Modified:	14 Aug 2020 03:24
URI:	http://eprints.ums.ac.id/id/eprint/84717

Actions (login required)

View Item