Anggi Prasetyo, Dika and , Joko Sedyono, ST, M.Eng, Ph.D and , Ir. Agus Hariyanto, MT (2016) Pengembangan Komposit Bermatrik Ebonit Dengan Kandungan Sulfur 30 Phr Yang Diperkuat Serat Kelapa Untuk Komponen Otomotif. Diploma thesis, Universitas Muhammadiyah Surakarta.
![]() |
PDF (Naskah Publikasi)
Naskah publikasi Dika.pdf Download (1MB) |
![]() |
PDF (Halaman Depan)
Halaman depan.pdf Download (955kB) |
![]() |
PDF (Bab I)
BAB I.pdf Download (167kB) |
![]() |
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (585kB) |
![]() |
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (1MB) |
![]() |
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (980kB) |
![]() |
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (149kB) |
![]() |
PDF (Daftar Pustaka)
daftar pustaka.pdf Download (116kB) |
![]() |
PDF (Lampiran)
Lampiran.pdf Restricted to Repository staff only Download (2MB) |
![]() |
PDF (Pernyataan Publikasi)
Surat Pernyataan.pdf Restricted to Repository staff only Download (534kB) |
Abstract
This study was aimed to determine the strength of the composite using a variation of fiber weight 0 phr, 30 phr and 50 phr by conducting a tensile test to ASTM D638, Izod test impact with ASTM D256, hardness test with the standard ISO 0778: 2009 and SEM photo by using JEOL JSM-6510LA tool. Composite materials used were ebonite as a matrix with coconut fiber reinforcement. The first process performed was the selection of coconut fibers which then cut as length as 20 mm and then fibers were soaked with NaOH 5% per 1 liter of distilled water with immersion time for 2 hours, after soaking finished coconut fibers were dried until the moisture content comes to 8%, then the process of compound production was ended by mixing natural rubber of chemicals materials and fibers using a two-roll mill, and then the vulcanizing was processed by using the hot press print method (hot press mold}. The results of the study showed that by the maximum tensile strength fiber composite with a weight of 30 phr with a voltage of 6.20 N / mm2, the maximum strain on the composite with 30 phr fiber weight by 84%. Average Izod impact testing ensued the highest average fiber weight 30 phr of 29.57 J / mm2, for the average hardness test results obtained the highest average fiber weight of 73.100 scale of 0 phr shore A and the SEM images obtained from composites with fraction of fiber weight 0 phr had the best structure. Keywords: composite, ebonite, coconut fiber, two roll mill, vulcanization
Item Type: | Karya ilmiah (Diploma) |
---|---|
Uncontrolled Keywords: | composite, ebonite, coconut fiber, two roll mill, vulcanization |
Subjects: | T Technology > TJ Mechanical engineering and machinery |
Divisions: | Fakultas Teknik > Teknik Mesin |
Depositing User: | DIKA ANGGI PRASETYO |
Date Deposited: | 05 Nov 2016 01:38 |
Last Modified: | 05 Nov 2016 01:38 |
URI: | http://eprints.ums.ac.id/id/eprint/47815 |