Adha, Rinanto Rizky and , Ir. Agung Setyo Darmawan, S.T., M.T., IPM. (2023) Pengaruh Sputtering Terhadap Ketahanan Korosi Baja AISI 410. Skripsi thesis, Universitas Muhammadiyah Surakarta.
![[img]](https://eprints.ums.ac.id/style/images/fileicons/application_pdf.png) |
PDF (Halaman Depan)
Halaman Depan.pdf Download (1MB) |
|
PDF (Bab I)
BAB I.pdf Download (190kB) |
|
PDF (Bab II)
BAB II.pdf Restricted to Repository staff only Download (591kB) |
|
PDF (Bab III)
BAB III.pdf Restricted to Repository staff only Download (595kB) |
|
PDF (Bab IV)
BAB IV.pdf Restricted to Repository staff only Download (637kB) |
|
PDF (Bab V)
BAB V.pdf Restricted to Repository staff only Download (182kB) |
|
PDF (Daftar Pustaka)
Daftar Pustaka.pdf Download (86kB) |
|
PDF (Lampiran)
Lampiran.pdf Restricted to Repository staff only Download (4MB) |
|
PDF (Naskah Publikasi)
Naskah Publikasi.pdf Download (582kB) |
|
PDF (Surat Pernyataan Publikasi)
Surat Pernyataan Publikasi.pdf Restricted to Repository staff only Download (195kB) |
Abstract
The sputtering process is a PVD (Physical Vapor Deposition) process which has been proven to increase surface hardness and coating on the surface of both metal, non-metal, ceramic and polymer materials. This study aims to determine the corrosion resistance of AISI 410 steel raw material and to determine the effect of sputtering on the corrosion resistance of AISI 410 stainless steel from annealing results. The technique used is plasma sputtering with tungsten nitride (WN) as the target. Sputtering is done in 120 minutes processing time. Then the corrosion test was carried out using the potentiostat electrochemical method to determine its corrosion resistance. From the results of corrosion testing, the acquisition of increased corrosion resistance after plasma sputtering was carried out. The raw material corrosion rate was 1.0439E-06 mmpy and the corrosion test results obtained after plasma sputtering were 3.43074E-07 mmpy.
| Item Type: | Thesis (Skripsi) |
|---|---|
| Uncontrolled Keywords: | Baja AISI 410, Annealing, Plasma sputtering (WN), Korosi |
| Subjects: | T Technology > TJ Mechanical engineering and machinery T Technology > TP Chemical technology T Technology > TS Manufactures |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | RINANTO RIZKY ADHA |
| Date Deposited: | 23 Aug 2023 05:20 |
| Last Modified: | 21 Dec 2023 02:42 |
| URI: | http://eprints.ums.ac.id/id/eprint/116903 |
Actions (login required)
 |
View Item |