Setiawan, Andi Dwi and -, Agus Yulianto, S. T., M. T. (2022) Pengaruh Inokulasi Nikel dan Magnesium 1%, 2%, 3%, 4% Terhadap Kekerasan Dan Struktur Mikro Besi Cor Ductile Pada Pengecoran Dinding Tipis Ketebalan 2 Milimeter. Skripsi thesis, Universitas Muhammadiyah Surakarta.
![[img]](http://eprints.ums.ac.id/style/images/fileicons/application_pdf.png) |
PDF (Naskah Publikasi)
Naskah Publikasi Andi DS-3.pdf Download (921kB) |
|
PDF (Halaman Depan)
HALAMAN DEPAN NEW-2hhhhjk.pdf Download (591kB) |
|
PDF (Bab I)
BAB 1 NEW.pdf Download (110kB) |
|
PDF (Bab II)
BAB 2 NEW.pdf Restricted to Repository staff only Download (488kB) |
|
PDF (Bab III)
BAB 3 NEW.pdf Restricted to Repository staff only Download (1MB) |
|
PDF (Bab IV)
BAB 4 NEW .pdf Restricted to Repository staff only Download (541kB) |
|
PDF (Bab V)
BAB 5 NEW.pdf Restricted to Repository staff only Download (34kB) |
|
PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf Download (94kB) |
|
PDF (Lampiran)
LAMPIRAN.pdf Restricted to Repository staff only Download (3MB) |
|
PDF (Surat Pernyataan Publikasi)
SURAT PERNYATAAN 11.pdf Restricted to Repository staff only Download (402kB) |
Abstract
The use of materials that can withstand high temperatures is usually stainless steel and cast steel is often used. Cast steel has the disadvantage of being able to cast lower than cast iron. Although cast iron has a higher castability, it also has a weakness for its thin thickness, its phase structure tends to change from graphite to cementite. Cast iron casting at a thin thickness will result in white cooling so that the phase is difficult to form graphite. Ductile cast iron has a spherical graphite shape. This research is to characterize thin and high temperature ductile cast iron material. The research was conducted by casting gray cast iron and inoculated with FeSiMg plus Nickel. The mold is made ladder with 4 thickness variations. Testing the chemical composition of solid conditions with a spectrometer with ASTM E415-8 standard for ductile/nodular cast iron. Microstructure testing with Microscope Optic ASTM E407 and hardness with Brinell ASTM E10
| Item Type: | Thesis (Skripsi) |
|---|---|
| Additional Information: | Publish |
| Uncontrolled Keywords: | Ductile cast iron, inoculation, thin wall |
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | ANDI DWI SETIAWAN |
| Date Deposited: | 24 Sep 2022 04:18 |
| Last Modified: | 24 Sep 2022 04:18 |
| URI: | http://eprints.ums.ac.id/id/eprint/104838 |
Actions (login required)
 |
View Item |