Pengaruh Alur Pahat (Toolpath) Terhadap Kekasaran Permukaan Hasil Pemesinan CNC Miling Router 3 Axis Pada Pembuatan Souvenir Dengan Media Acrilyc

Oktavianto. Kp, Randy and , Bambang Waluyo F, ST., MT. (2022) Pengaruh Alur Pahat (Toolpath) Terhadap Kekasaran Permukaan Hasil Pemesinan CNC Miling Router 3 Axis Pada Pembuatan Souvenir Dengan Media Acrilyc. Skripsi thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) NASKAH PUBLIKASI.pdf Download (837kB)
	PDF (Halaman Depan) HALAMAN DEPAN.pdf Download (444kB)
	PDF (Bab I) BAB I.pdf Download (81kB)
	PDF (Bab II) BAB II.pdf Restricted to Repository staff only Download (483kB) | Request a copy
	PDF (Bab III) BAB III.pdf Restricted to Repository staff only Download (1MB) | Request a copy
	PDF (Bab IV) BAB IV.pdf Restricted to Repository staff only Download (354kB) | Request a copy
	PDF (Bab V) BAB V.pdf Restricted to Repository staff only Download (8kB) | Request a copy
	PDF (Daftar Pustaka) DAFTAR PUSTAKA.pdf Download (52kB)
	PDF (Surat Pernyataan Publikasi) SURAT PERNYATAAN.pdf Restricted to Repository staff only Download (96kB) | Request a copy

Abstract

This study aims to determine the effect of Asem wood charcoal in the heat treatment process using the carburizing method on SS 400 steel on mechanical properties and microstructure.In this study, the carburizing medium used was tamarind wood charcoal with a weight percentage of 60% and a CaCo3 catalyst of 40%. The temperature used is 8500C with a holding time of 60 minutes with a variation of 15w-40 oil and water quenching media.The results of the tensile test show that the carburizing material with variations of oil and water quenching media has more brittle properties than the raw material. The surface hardness value for raw material is 191.53 VHN, while for carburizing material with oil quenching media it is 412.00 VHN, while for carburizing material with water quenching media it is 508.64 VHN. The results of micro photos of carburizing material with water quenching media have a pearlite phase which is more dominant than raw material and carburizing material with oil quenching media.

Item Type:	Thesis (Skripsi)
Uncontrolled Keywords:	carburizing, quenching, tensile, hardness, microstructure.
Subjects:	T Technology > T Technology (General) T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username d200217309
Date Deposited:	28 May 2022 06:55
Last Modified:	28 May 2022 06:55
URI:	http://eprints.ums.ac.id/id/eprint/100898

Actions (login required)

View Item