Karakterisasi Material Besi Cor Kelabu Akibat Pengaruh FeSi 4% + FeMn 4% Pada Proses Casting dengan Cetakan Logam dan Pasir

Wicaksena, Novfian Rekzy and , Agus Yulianto, ST, MT (2021) Karakterisasi Material Besi Cor Kelabu Akibat Pengaruh FeSi 4% + FeMn 4% Pada Proses Casting dengan Cetakan Logam dan Pasir. Skripsi thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
NASKAH PUBLIKASI (34).pdf

Download (1MB)
[img] PDF (Halaman Depan)
HALAMAN DEPAN (65).pdf

Download (2MB)
[img] PDF (Bab I)
BAB I (29).pdf

Download (247kB)
[img] PDF (Bab II)
BAB II.pdf
Restricted to Repository staff only

Download (595kB) | Request a copy
[img] PDF (Bab III)
BAB III.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] PDF (Bab IV)
BAB IV.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] PDF (Bab V)
BAB V.pdf
Restricted to Repository staff only

Download (191kB) | Request a copy
[img] PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf

Download (296kB)
[img] PDF (Lampiran)
LAMPIRAN.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] PDF (Surat Pernyataan Publikasi)
pernyataan publikasi.pdf
Restricted to Repository staff only

Download (236kB) | Request a copy

Abstract

This study aims to determine the characterization of gray cast iron material due to the effect of FeSi 4% + FeMn 4% on the casting process with iron mold and sand mold. The material was made using gray cast iron with a variation of the element FeSi 4% + FeMn 4%. The manufacturing process uses the sand casting method using metal molds and sand molds. Then the material from the casting is cut and then tested using the hardness testing method, microstructure and SEM EDS. The result of this test, the highest hardness lies in the bottom metal mold which has an average hardness of 259 BHN and the lowest toughness is located in the upper sand mold, which has an average hardness of 184 BHN. In the microstructure test, the results obtained were ferrite and pearlite phases, dominated by the pearlite phase and obtained smooth and elongated graphite. In the SEM test at 2000x magnification, it was seen that the density in the metal mold was smoother than in the sand mold.

Item Type: Karya ilmiah (Skripsi)
Uncontrolled Keywords: cast iron, silicon, manganese, sand casting, microstructure.
Subjects: T Technology > TS Manufactures
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: NOVFIAN REKZY WICAKSENA
Date Deposited: 12 Aug 2021 06:36
Last Modified: 12 Aug 2021 06:36
URI: http://eprints.ums.ac.id/id/eprint/92997

Actions (login required)

View Item View Item