Pengaruh Penambahan Timah Hitam (Pb) sebesar 20% pada Pengecoran menggunakan Bahan Aluminium Ukuran 10x10 cm dengan Media Cetak Pasir Merah

Hermawan, Rian Candra and , Agus Yulianto, ST, MT (2019) Pengaruh Penambahan Timah Hitam (Pb) sebesar 20% pada Pengecoran menggunakan Bahan Aluminium Ukuran 10x10 cm dengan Media Cetak Pasir Merah. Skripsi thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
NASKAH PUBLIKASI.pdf

Download (265kB)
[img] PDF (Halaman Depan)
HALAMAN DEPAN.pdf

Download (273kB)
[img] PDF (Bab I)
BAB I.pdf

Download (30kB)
[img] PDF (Bab II)
BAB II.pdf
Restricted to Repository staff only

Download (352kB) | Request a copy
[img] PDF (Bab III)
BAB III.pdf
Restricted to Repository staff only

Download (224kB) | Request a copy
[img] PDF (Bab IV)
BAB IV.pdf
Restricted to Repository staff only

Download (117kB) | Request a copy
[img] PDF (Bab V)
BAB V.pdf
Restricted to Repository staff only

Download (20kB) | Request a copy
[img] PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf

Download (11kB)
[img] PDF (Lampiran)
LAMPIRAN.pdf
Restricted to Repository staff only

Download (229kB) | Request a copy
[img] PDF (Surat Pernyataan Publikasi)
SURAT PERNYATAAN PUBLIKASI.pdf
Restricted to Repository staff only

Download (46kB) | Request a copy

Abstract

This study aims to determine the effect of adding 20% of Black Tin (Pb) to aluminum casting on the quality of cast products for brinell hardness, chemical composition, microstructure and porosity. will affect the quality of the cast product. This study uses aluminum (Al) used or scrubbed with a weight of 2000 grams and an additional lead (Pb) of 20% of the weight of aluminum melted back using a smelting kitchen. The print media used is red sand. Hardness testing uses the ASTM E10 standard and Microstructure test using ASTM E3. The results of the brinell hardness test of cast products without mixture were 88,832 BHN, while the cast products with lead mixture were 20%, 98,599 BHN. Judging from the microstructure of the castings the most dominant element is Al and Si, where the production of non-mixtures has more Si grains than the lead mixture of 20%. From the results of testing the chemical composition there are 15 elements, with the most dominant element being Si at 8.3182%, Zn at 3.2731%, Cu at 1.9865% and Pb at 1.8517% while aluminum (Al) at 83, 74%. In cast products with a mixture of 20% lead has 15 elements, with the most dominant element Si is 7.7848% and Zn is 2.9240%, Cu is 2.2722% and Pb is 1.9746% while aluminum is 83.84 %.

Item Type: Karya ilmiah (Skripsi)
Uncontrolled Keywords: Timah Hitam, Pengecoran, Aluminium
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: RIAN CANDRA HERMAWAN
Date Deposited: 24 Apr 2019 04:09
Last Modified: 24 Apr 2019 04:09
URI: http://eprints.ums.ac.id/id/eprint/72176

Actions (login required)

View Item View Item