Pengaruh Komposisi Ampas Tebu (Bagasse) dan Resin Epoxy dengan Pelapisan Menggunakan Larutan Hydroxymethylated resorcinol (HMR) terhadap Karakteristik Komposit

Ahlina, Darari Nur and , Hamid Abdillah, S.T., M.T. (2019) Pengaruh Komposisi Ampas Tebu (Bagasse) dan Resin Epoxy dengan Pelapisan Menggunakan Larutan Hydroxymethylated resorcinol (HMR) terhadap Karakteristik Komposit. Skripsi thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
Darari Nur Ahlina_D500170041.pdf

Download (475kB)
[img] PDF (Pernyataan Publikasi Ilmiah)
Pernyataan publikasi.pdf
Restricted to Repository staff only

Download (212kB) | Request a copy

Abstract

Composites are materials formed from two or more components which are combined as macroscopic structural units with one component as a matrix and the other as reinforcing fibers. Baggase is a pulp from sugar cane which has been extracted from sugar. Bagasse has a proper tensile strength and modulus of elasticity. The thermosetting matrix used in the research is epoxy resin because epoxy has a high level of strength and toughness. The composites will be cross linking with hydroxymethylated resorcinol (HMR) solution in the bagasse. Bagasse coated with an HMR solution can increase the tensile strength of the composite. The independent variables used are bagasse composition of 4%; 8%; and 12%, epoxy resin by 96%; 92%; and 88% and bagasse coating using 5 ml / gram bagasse HMR solution; 7,5 ml / gram bagasse and without coating HMR solution. Bagasse is created using the method of making hand lay-ups. In this process, bagasse is inserted manually into the mold, then the resin is flattened using a hand roll to all layers of fiber. After the composite is finished, then the tensile strength and modulus elasticity are tested. The highest tensile strength of 9 experiments was found in the second variable (bagasse 8%, resin 92%) with a coating of HMR 7 ml / gram bagasse solution of 1,916 MPa. The highest modulus of elasticity is in variable 1 (bagasse 4%, resin 96%) without coating HMR solution of 160,076 MPa.

Item Type: Karya ilmiah (Skripsi)
Uncontrolled Keywords: bagasse, resin epoksi, komposit, hydroxymethylated resorcinol (HMR)
Subjects: Q Science > QD Chemistry
Divisions: Fakultas Teknik > Teknik Kimia
Depositing User: DARARI NUR AHLINA
Date Deposited: 15 Jan 2019 07:34
Last Modified: 15 Jan 2019 07:34
URI: http://eprints.ums.ac.id/id/eprint/69717

Actions (login required)

View Item View Item