Pengaruh Inokulasi Mangan Pada Besi Cor Kelabu Terhadap Kekuatan Tarik

Nugroho, Adi and -, Agus Yulianto, ST., MT (2016) Pengaruh Inokulasi Mangan Pada Besi Cor Kelabu Terhadap Kekuatan Tarik. Diploma thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (Naskah Publikasi)
PUBLIKASI.pdf

Download (1MB)
[img] PDF (Halaman Depan)
COVER HALAMAN DEPAN.pdf

Download (809kB)
[img] PDF (Bab I)
BAB 1.pdf

Download (166kB)
[img] PDF (Bab II)
BAB II.pdf
Restricted to Repository staff only

Download (348kB) | Request a copy
[img] PDF (Bab III)
BAB III.pdf
Restricted to Repository staff only

Download (683kB) | Request a copy
[img] PDF (Bab IV)
BAB IV.pdf
Restricted to Repository staff only

Download (473kB) | Request a copy
[img] PDF (Bab V)
BAB V.pdf
Restricted to Repository staff only

Download (89kB) | Request a copy
[img] PDF (Lampiran)
LAMPIRANN.pdf
Restricted to Repository staff only

Download (3MB) | Request a copy
[img] PDF (Daftar Pustaka)
DAFTAR PUSTAKA.pdf

Download (113kB)
[img] PDF (Surat pernyataan publikasi ilmiah)
Surat PernyataanADHI.pdf
Restricted to Repository staff only

Download (510kB) | Request a copy

Abstract

This study aims to determine the effect of inoculation of manganese in gray cast iron to strength power. This study uses sand molds with cylindrical wood pattern. Methodology this study is done with cast iron melting in induction fireplace and then is poured in sand molds for making gray cast iron specimen. This research to determine the melting temperature and chemical composition C and silicon in the form of liquid gray cast iron using test equipment CE Meter then the gray cast iron specimen research the chemical composition and power strength research and then the hardness test and micro photo. The result of the research is a chart obtained from CE METER shows the temperature 1315.2 0C during tapping beginning poured into the mold. A decrease in temperature of up to 1155.2 0C, 1315.2 0 C form is a liquid metal with CEL value = 4.17%; C = 3.60%; Si = 2.24%. After the temperature 1155.20 C metal begins to freeze. The metal freeze all at temperatures 1113.20 C, on the condition of the red metal. On the results of the chemical composition contained 20 kinds, but only 6 elements which can influence on cast iron are Fe, CSi, Mn, Cr and Ni. In the picture shows the graphite microstructure, perlite and cementite, which affected the price of hardness. Power test results showed the addition of Mn got the highest of 209,81 N / mm2 and the results obtained 41.14 HRB hardness. Based on these data it can be concluded that the addition of manganese can increase the hardness and power strength. Keywords : inoculation, gray cast iron, CE meter, tensile testing, hardness

Item Type: Thesis (Diploma)
Uncontrolled Keywords: inoculation, gray cast iron, CE meter, tensile testing, hardness
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: ADHI NUGROHO
Date Deposited: 05 Nov 2016 03:14
Last Modified: 05 Nov 2016 03:14
URI: http://eprints.ums.ac.id/id/eprint/47814

Actions (login required)

View Item View Item