STUDI SIFAT FISIS DAN MEKANIS PADA SOLIDIFIKASI BESI COR KELABU DALAM CETAKAN PERMANEN UNTUK TAPPING AKHIR

SUPRIYANTO, HERI and , Ir. H. Masyrukan, MT (2016) STUDI SIFAT FISIS DAN MEKANIS PADA SOLIDIFIKASI BESI COR KELABU DALAM CETAKAN PERMANEN UNTUK TAPPING AKHIR. Diploma thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (NASKAH PUBLIKASI)
10. NASKAH PUBLIKASI.pdf

Download (1MB)
[img] PDF (HALAMAN DEPAN)
02. HALAMAN DEPAN.pdf

Download (4MB)
[img] PDF (BAB 1)
03. BAB 1.pdf

Download (106kB)
[img] PDF (BAB 2)
04. BAB 2.pdf
Restricted to Repository staff only

Download (1MB)
[img] PDF (BAB 3)
05. BAB 3.pdf
Restricted to Repository staff only

Download (380kB)
[img] PDF (BAB 4)
06. BAB 4.pdf
Restricted to Repository staff only

Download (318kB)
[img] PDF (BAB 5)
07. BAB 5.pdf
Restricted to Repository staff only

Download (21kB)
[img] PDF (DAFTAR PUSTAKA)
08. DAFTAR PUSTAKA.pdf

Download (159kB)
[img] PDF (LAMPIRAN)
09. LAMPIRAN.pdf

Download (3MB)
[img] PDF (SURAT PERNYATAAN PUBLIKASI KARYA ILMIAH)
01. SURAT PERNYATAAN PUBLIKASI KARYA ILMIAH.pdf
Restricted to Repository staff only

Download (186kB)

Abstract

This research took a part of metal casting, that was a matter of melting which aimed at knowing the influene of the melting of grey cast iron in the final tapping with a high frequency induction on the values of hardness, micro structure and chemical composition. This research was conducted on the specimen of greay cast iron testing from a permantent mold. The testings conducted were a testing of chemical composition using spectrometer, a testing of hardness through the rockwell method using a hardness testinger converted into the hardness brinell method, and the testing of micro structure using a metalography microscope. From the results of the testing of specimen, it was obtained that the bahwa specimen of grey cast iron has several chemical composition, they were: carbon (C): 3.52%, silicon (Si): 1.95%, manganese (Mn): 0.,470%, etc. The hardness testing was conducted on two sides: the upper-part testing and the side part testing, each had 5 testing points. In the side part, it was obtained the hardness values (223,79; 226,97; 224,12; 232,44; 227,03). it was obtained the average hardness value as much as 226,02. In the upper-part, it was obtained the hardness value (441,14; 432,50; 430,32; 439,58; 425,86) and the average value 433,12

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Pengujian, besi cor, tapping akhir
Subjects: T Technology > TS Manufactures
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: Heri Supriyanto
Date Deposited: 13 Aug 2016 06:48
Last Modified: 13 Aug 2016 06:48
URI: http://eprints.ums.ac.id/id/eprint/45877

Actions (login required)

View Item View Item