Karakteristik Komposit Serbuk Kayu Jati Dengan Fraksi Volume 25%, 30%, 35% Terhadap Uji Bending, Uji Tarik Dan Daya Serap Bunyi Untuk Dinding Peredam Suara

Krisdianto, Andi and , Wijianto, ST, M.Eng, Sc. and , Pramuko IP, Ir, MT. (2016) Karakteristik Komposit Serbuk Kayu Jati Dengan Fraksi Volume 25%, 30%, 35% Terhadap Uji Bending, Uji Tarik Dan Daya Serap Bunyi Untuk Dinding Peredam Suara. Diploma thesis, Universitas Muhammadiyah Surakarta.

	PDF (Naskah Publikasi) 02. Naskah Publikasi.pdf Download (1MB)
	PDF (Halaman Depan) 03. Halaman Depan.pdf Download (3MB)
	PDF (BAB I) 04. BAB I.pdf Download (155kB)
	PDF (BAB II) 05. BAB II.pdf Restricted to Repository staff only Download (349kB) | Request a copy
	PDF (BAB III) 06. BAB III.pdf Restricted to Repository staff only Download (315kB) | Request a copy
	PDF (BAB IV) 07. BAB IV.pdf Restricted to Repository staff only Download (294kB) | Request a copy
	PDF (BAB V) 08. BAB V.pdf Restricted to Repository staff only Download (89kB) | Request a copy
	PDF (Daftar Pustaka) 09. DAFTAR PUSTAKA.pdf Download (5kB)
	PDF (Lampiran) 10. Lampiran.pdf Restricted to Repository staff only Download (8MB) | Request a copy
	PDF (Pernyataan Publikasi Ilmiah) 01. Surat Pernyataan Publikasi Ilmiah.pdf Restricted to Repository staff only Download (83kB) | Request a copy

Abstract

Purpose of the research is to know tensile strength and bending strength of teakwood dust composite with volume fractions of 25%, 30% and 35% according to ASTM D 3039-00 standards and ASTM D 790-99 standards and to know capacity value of sound absorption with sponge and plywood linings according to ANSI S1 13-05 standards. Primary material of the research is teakwood sawdust with matrix of Fox PVAc adhesive substance. Main variable of the research is fractions of sawdust volume of 25%, 30% and 35% with procedures of the tensile strength is referred to ASTM D 3039-00, the bending strength is referred to ASTM D 790-99 and test of sound absorption is referred to ANSI S1. 13-05. Results of the research showed that the highest average tensile strength of 1.95 Mpa was found at volume fraction of 25% and modulus of elasticity of 20.23 Mpa, whereas the lowest tensile strength of 1.03 Mpa was found at volume fraction of 35% and modulus of elasticity of 20.23 Mpa. The highest bending strength of 11.98 Mpa was found at 25% and modulus of elasticity of 112.73, whereas the lowest bending strength of 9.46 Mpa was found at volume fraction of 35% and modulus of elasticity of 74.22 Mpa. The highest value of the sound absorption without sponge and plywood linings was found at volume fraction of 35%, namely 2.36 dB, whereas the lowest one of 0.90 dB was found at volume fraction of 25%. The highest value of sound absorption with sponge and plywood linings was found at volume fraction 35%, namely 2.07 dB and the lowest one was found at volume fraction 25%, namely 1.05 dB,

Item Type:	Karya ilmiah (Diploma)
Uncontrolled Keywords:	composite, teakwood sawdust, volume fraction, panel of sound absorptio
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	ANDI KRISDIANTO
Date Deposited:	11 Aug 2016 01:36
Last Modified:	11 Aug 2016 01:36
URI:	http://eprints.ums.ac.id/id/eprint/45452

Actions (login required)

View Item