Analisis Komposit Dengan Penguat Serat Nanas 40% Dan Serbuk Kayu Sengon 60% Pada Fraksi Volume 40%,50%,60% Bermatrik Resin Polyester Untuk Panel Akuistik

Kristiyanto, Kristiyanto and , Wijianto, ST. MEng. Sc. and , Ir. Bibit Sugito, MT (2016) Analisis Komposit Dengan Penguat Serat Nanas 40% Dan Serbuk Kayu Sengon 60% Pada Fraksi Volume 40%,50%,60% Bermatrik Resin Polyester Untuk Panel Akuistik. Diploma thesis, Universitas Muhammadiyah Surakarta.

[img] PDF (HALAMAN DEPAN)
HALAMAN JUDUL.pdf

Download (1MB)
[img] PDF (BAB I)
BAB I.pdf

Download (111kB)
[img] PDF (BAB II)
BAB II.pdf
Restricted to Repository staff only

Download (589kB) | Request a copy
[img] PDF (BAB III)
BAB III.pdf
Restricted to Repository staff only

Download (734kB) | Request a copy
[img] PDF (BAB IV)
BAB IV.pdf
Restricted to Repository staff only

Download (737kB) | Request a copy
[img] PDF (BAB V)
BAB V.pdf
Restricted to Repository staff only

Download (196kB) | Request a copy
[img] PDF (DAFTAR PUSTAKA)
DAFTAR PUSTAKA.pdf

Download (190kB)
[img] PDF (LAMPIRAN)
LAMPIRAN.pdf
Restricted to Repository staff only

Download (6MB) | Request a copy
[img] PDF (SURAT PERNYATAAN PUBLIKASI)
PERNYATAAN PUBLIKASI.pdf
Restricted to Repository staff only

Download (427kB) | Request a copy
[img] PDF (Naskah Publikasi)
NASKAH PUBLIKASI_kris1.pdf

Download (1MB)

Abstract

Purpose of the research is to know tensile strength, bending and acoustic impedance of pineapple fiber composite at volume fraction of (40%, 50%, and 60%). The composite is made by using mold press method. The composite is made from pineapple fiber and sengon sawdust with polyester resin of Yukalac 157 BQTN – EX and MEKPO catalyst, and volume fraction variation of 40%, 50%, 60%. Press mold was used to make the composite. The composite was tested according to ASTM D 638-02 standard. ASTM D790-02 for tensile strength and ANSI S1-13 for acoustic impedance test. Results of the research indicated that average tensile strength at volume fraction of 60% was 34.680 MPa and lowest result at fraction of 40% was 27.189 MPa. The highest averaged elasticity modulus was found at volume fraction of 60%, namely 46.240 MPa and, the lowest one was at fraction volume of 40%, namely 45.315 MPa. Results of tensile strength testing were: the highest averaged tensile strength of 57.504 MPa was found at fraction of 60% and the lowest one of 39.166 MPa was found at fraction of 40%. Results of acoustic impedance with spon were: the highest results were found at volume fraction of 50%, namely 62.06 dB and the lowest one was found at fraction of 60%, namely 61.89 dB. Then, results without spon found the highest at fraction of 50%, 62.07 dB and the lowest was found at fraction of 40%, 61.81 dB Key words: Tensile strength, bending test, acoustic impedance

Item Type: Karya ilmiah (Diploma)
Uncontrolled Keywords: Uji Tarik, Uji Bending, Impedansi Akuistik
Subjects: Q Science > Q Science (General)
Divisions: Fakultas Teknik > Teknik Mesin
Depositing User: KRISTIYANTO
Date Deposited: 09 Aug 2016 03:35
Last Modified: 09 Aug 2016 03:35
URI: http://eprints.ums.ac.id/id/eprint/45215

Actions (login required)

View Item View Item